Limestone is an important component in glassmaking and is used as a stabilizer which improves the mechanical properties and physical appearance of the glass.

Specifications for Limestone in Glassmaking

Glass industry required high limestone (CaCO3: 94.5%) combined CaCO3 and MgCO3 should be 97.5%. Iron and other colouring matter like carbon are regarded as objectionable. Fe2O3 should be up to 0.20% (max.). For colourless glass, limestone should not be more than 0.04%; and for bottle glass Fe2O3 up to 0.05% is used.

Limestone is ideal for the glass industry as it has a high purity with very low levels of undesirables and contaminants that would be detrimental to the glass making process. It has a very low Iron content typically < 0.03% Fe2O3 with high Calcium content in the order of 98.5% CaCO3 and with the added advantage of consistent Magnesium content typically of 1% MgCO3. The Limestone that is produced can have both economic and environmental benefits to the glass producer.

We currently produce high-quality limestone for the manufacture of container glassware worldwide.

Commercial Glass Making

The majority of commercial glasses, bottles and jars consist of Soda-Lime Glass. Soda-Lime glass is the most common type of glass produced for glass containers (bottles and jars) for beverages, food, and some commodity items. Silica sand, soda ash and calcium limestone or dolomitic limestone represent together with a majority of the raw materials used in the production of glass.

Soda-Lime glass is generally prepared by melting the raw materials or batch, such as Silica Sand (Silicon Dioxide, SiO2) with Soda Ash (Sodium carbonate, Na2CO3), Limestone or Dolomite (Calcium Carbonate, CaCO3) plus a small percentage of other materials can be added for specific properties such as colouring. The composition of soda-lime glass is normally 60-75% silica, 12-15% soda, and 5-12% lime.

The glass batch once produced is fed into the glass furnaces where temperatures can be in excess of 1500 °C. Green and brown bottles are obtained from raw materials containing iron oxide, whereas clear glass bottles are obtained from the lack of colouring agents.

Normally, sand melts and softens at temperatures of up to 2000°C, by adding soda this will act as a flux and will lower the melting point to 1000°C making it more manageable. The soda makes the glass water-soluble, soft and not very durable. Therefore the limestone is added to act as a stabilizer and increases the hardness and chemical durability of the glass.

Soda-lime glass is relatively inexpensive, chemically stable, reasonably hard, and extremely workable because it is capable of being re-softened and re-melted numerous times, ideal for recycling. These qualities make it suitable for manufacturing a wide array of glass products, including bottles. All glass bottles and jars are now made automatically by one of two methods – ‘Press and Blow’ or ‘Blow and Blow’ using compressed air.